Mochine oa khatello ke khoebo e kholo ka ho fetisisa ea HC, mme re khethehile ka mochine oa SMC / BMC / GMT / LFT / HP-RTM ka lilemo tse fetang leshome.
SMC ke motsoako oa resine ea polymeri, kenya li-fillers, fiber reinforcement, catalyst, pigments, stabilizers, li-release, le li-thickeners. Ho hlahisoa ha SMC ke ts'ebetsong ea ts'ebetso e tsoelang pele.
This process produces high strength, complex parts in a wide variety of sizes. Matched metal dies are mounted in a hydraulic molding press. Thematerial charge is manually or robotically placed in the mold; the heated mold halves are closed, and up to 2000 psi of pressure is applied. Cycle time ranges from one to five minutes, depending on part size and thickness. Features such as ribs, bosses and inserts can be molded in.
Compression molded fiberglass parts are characterized by net size and shape, two excellent finished surfaces, and outstanding parts-to-part repeatability. Trimming and finishing costs are minimal.
In-mold coatings and vacuum system in the tool are available to improve surface paint ability, eliminating the need for primer.
Color compounds can be customized.
Theadvantage of SMC molding parts is as follows:
1. Ho ba le botsitso bo botle ba lefats'e, ho kenyeletsa le ho ba le mefuta e metle ea lichelete.
2. Pigmentable bakeng sa 'mala o bōpehileng, o motle ka ponahalo ea hlobo.
3. Excellent property retention in cold and hot environments.
4. Suitable for outdoor use in applications involving UV exposure and water.
BMC mold used a thermoset plastic made up of a polymer resin, various insert fillers, fiber reinforcement, catalysts, stabilizers, and pigments that form a viscous. It is highly filled and reinforced with short fibers.
BMC is available in bulk bags as well as slug form. Themixing operation can be done in a number of ways. There are three methods for combining glass with paste: a continuous screw mixer, a sigma blade mixer and a plough blade mixer. Theprocess chosen is dependent upon specific product properties, product form and volume.
Depending on the end-use application, compounds are formulated to achieve tight dimensional control, flame resistance, high dielectric strength, corrosion and stain resistance and color stability. Its excellent flow characteristics make BMC mold well suited to a wide variety of applications requiring precision in detail and dimensions. Thematerial is available in a wide variety of colors.
Besides, BMC mold is suitable for either compression molding or injection molding. Compressing molding of BMC is used to produce complex components such as electrical equipment, car components, housings for electrical appliances and tools, in large industrial volumes.
GMT is Glass Mat Reinforced Thermoplastics, mofuta oa lekhabiso le nang le fiber e matlafatsang thermoplastic. E hlahisoa ka li-laminators tse kholo, ho sebelisa mocheso oa thermoplastic le mofuta o mong kapa mefuta e meng ea matlafatso. Mokhoa ona o hlahisa boima bo bobebe, bo kopantsoe ka mokhoa o itseng, bo nang le likarolo tse lekaneng tse lekaneng. Mefuta e mengata e hlahisoa ka bophara ba 1300mm ho ea ho 1400 mm. Leha ho le joalo, mefuta e meng e mecha e entsoe ka bophara bo bongata empa bo na le maiketsetso. Letšoao la lakane le ka fokotsoa hore le behoe ka har'a sesebelisoa sa sesebelisoa se khethehileng 'me le ka kenyelletsa sebaka se khabisitsoeng kapa se sebetsang se khabisitsoeng ka lehlakoreng le leng. GMT hlobo e nolofalletsa ho hlahisa likarolo tse kholo ka litšenyehelo tse tlaase tsa ho sebelisa lisebelisoa le linako tse potlakileng ka nako ea khatello ea lik'hemik'hale. Monyetla oa likarolo tse kopaneng o fana ka monyetla oa ho eketsa ho fokotsa boima le litšenyehelo.
Theadvantage of GMT hlobo parts: utilization of regenerated, low forming pressure, long storage period, short shaping cycle, high production efficiency.
GMT mold is mostly used in Automotive and building &construction, chemical industry, packaging, sport equipment, etc.
LFT is bulk molding material that feature continuous fiber filaments running the full length of the pellet allowing these materials to exhibit simultaneous improvements in strength, stiffness, and impact resistance over a wide temperature range.
Meanwhile, D-LFT (Direct-long fiber thermoplastics) is available for injection or compression molding. Most D-LFT systems, feed glass roving into a twin-screw extruder (TSE), where it is chopped by the screws as it is mixed with molten polymer and additives that have been metered in separately. To improve surface finish, some systems use knives to prechop the roving prior to entrance into the TSE. This method generally yields a shorter fiber, while the direct roving feed produces long fibers and yields parts with higher structural performance.
Theadvantage of D-LFT mold is that it can reduce production cost by elimination of semi-finished products and logistical effort, and increase production flexibility.
Since established in 1996, Huacheng Moulde fetisitse ISO9001 mme e buelloa hore e be se molemo ka ho fetisisaSMC/BMC/GMT/LFT/ LFI hlobo supplier in China. With the company philosophy of “Honesty, quality, and efficiency” which enable us to keep a long-term cooperation with our barekioverseas. Having the capability of design and making hlobos according to European technical standards and quality level, Huacheng has become one of the pillars of the industry.
We have successful experience in making various kinds of hlobos for:
Thebarekiea Huacheng Mold kehohle lefatšeng, joalo as America, Italy, Malaysia, Thailand, Iran le joalo-joalo. Our products enjoy the highest quality with the most reasonable price.